Name: Effect of Reversion Heat treatment on Duplex Stainless Steels (en Inglés)
Price: 258218.00 COP
Availability: InStock
Author: Vasantha Kumar, Shamanth ; Shankar K. S., Ravi
ISBN: 9786139952359

portada Effect of Reversion Heat treatment on Duplex Stainless Steels (en Inglés)

Formato

Libro Físico

Autor

Shamanth Vasantha Kumar

Ravi Shankar K. S.

Editorial

LAP Lambert Academic Publishing

Idioma

Inglés

N° páginas

136

Encuadernación

Tapa Blanda

Dimensiones

22.9 x 15.2 x 0.8 cm

Peso

0.21 kg.

ISBN13

9786139952359

Categorías

Ingeniería: general

Effect of Reversion Heat treatment on Duplex Stainless Steels (en Inglés)

Shamanth Vasantha Kumar (Autor) · Ravi Shankar K. S. (Autor) · LAP Lambert Academic Publishing · Tapa Blanda

Libro Nuevo

$ 258.218

$ 516.436

Ahorras: $ 258.218

50% descuento

Envío normal

Origen: Estados Unidos (Costos de importación incluídos en el precio)

Se enviará desde nuestra bodega entre el Martes 23 de Julio y el Martes 06 de Agosto.

Lo recibirás en cualquier lugar de Colombia entre 1 y 5 días hábiles luego del envío.

Reseña del libro "Effect of Reversion Heat treatment on Duplex Stainless Steels (en Inglés)"

The thermal aging embrittlement of duplex stainless steels is one of the key material property degradation that would limit their industrial applicability. In this investigation, we study the effect of reversion heat treatment on the mechanical properties of the thermally embrittled steels. The samples were solutionized, aged, reversion heat treated and re-aged. The tensile strength of the aged sample had increased with respect to the solutionized condition because in aged condition, the ferrite phase was spinodally decomposed into iron rich alpha (α) and chromium rich alpha-prime (αˈ) precipitates and also the chromium nitride precipitates was found along with these precipitates. The 60 minutes reversion heat treated samples showed a maximum recovery in tensile strength of upto 92% with respect to the solutionized condition because the temperature of 550 ⁰C is above the (α + αˈ) miscibility gap, the ferritic phase was homogenized again. In other words, Ferich α and Cr-rich αˈ prime precipitates which were formed during ageing become thermodynamically unstable and dissolve inside the ferritic phase.